Structures by: Zharikov E. V.
Total: 15
La Sc3 (B O3)4
B4LaO12Sc3
Zhurnal Neorganicheskoi Khimii (1996) 41, 1605-1611
a=7.727Å b=9.84Å c=12.046Å
α=90° β=105.42° γ=90°
Ca Y Al3 O7
Al3CaO7Y
Zhurnal Neorganicheskoi Khimii (1995) 40, 569-577
a=7.676Å b=7.676Å c=5.04Å
α=90° β=90° γ=90°
Ca Y (Al2.91 Cr0.09) O7
Al2.91CaCr0.09O7Y
Zhurnal Neorganicheskoi Khimii (1995) 40, 569-577
a=7.679Å b=7.679Å c=5.042Å
α=90° β=90° γ=90°
Ca Y Al2.91 Cr0.06 B0.03 O7
Al2.91B0.03CaCr0.06O7Y
Zhurnal Neorganicheskoi Khimii (1995) 40, 569-577
a=7.68Å b=7.68Å c=5.042Å
α=90° β=90° γ=90°
Ca2 Mg ((Si0.99 Cr0.01)2 O7)
Ca2Cr0.02MgO7Si1.98
Zhurnal Neorganicheskoi Khimii (1995) 40, 1422-1428
a=7.835Å b=7.835Å c=5.008Å
α=90° β=90° γ=90°
Ca2 Al (Al.5 B.5 Si.5 Cr.5 O7)
Al1.5B0.5Ca2Cr0.5O7Si0.5
Zhurnal Neorganicheskoi Khimii (1995) 40, 1422-1428
a=7.69Å b=7.69Å c=5.0714Å
α=90° β=90° γ=90°
Ca2 Al (Al (Si0.974 Cr0.026) O7)
Al2Ca2Cr0.026O7Si0.974
Zhurnal Neorganicheskoi Khimii (1995) 40, 1422-1428
a=7.6877Å b=7.6877Å c=5.0659Å
α=90° β=90° γ=90°
(Na0.24 Gd0.59 Yb0.17) (W O4)0.98
Gd0.59Na0.24O3.92W0.98Yb0.17
Neorganicheskie Materialy (2003) 39, 200-211
a=5.225Å b=5.225Å c=11.331Å
α=90° β=90° γ=90°
(Na0.5 Gd0.5) (W O4)0.78
Gd0.5Na0.5O3.12W0.78
Neorganicheskie Materialy (2003) 39, 200-211
a=5.225Å b=5.225Å c=11.326Å
α=90° β=90° γ=90°
(Na0.5 Gd0.5) (W O4)0.94
Gd0.5Na0.5O3.76W0.94
Neorganicheskie Materialy (2003) 39, 200-211
a=5.224Å b=5.224Å c=11.35Å
α=90° β=90° γ=90°
Li (Ga0.9 Cr0.1) O1.97
Cr0.1Ga0.9LiO1.97
Inorganic Materials (USSR) (see: Izv.Akad.Nauk, Neorg.Mater.) (2001) 37, 281-285
a=5.3956Å b=6.3675Å c=5.0024Å
α=90° β=90° γ=90°
Li (Ga O2)
GaLiO2
Inorganic Materials (USSR) (see: Izv.Akad.Nauk, Neorg.Mater.) (2001) 37, 281-285
a=5.395Å b=6.367Å c=5.005Å
α=90° β=90° γ=90°
Li (Ga0.967 V0.033) O2
Ga0.967LiO2V0.033
Inorganic Materials (USSR) (see: Izv.Akad.Nauk, Neorg.Mater.) (2001) 37, 281-285
a=5.3995Å b=6.3996Å c=5.006Å
α=90° β=90° γ=90°
Li (Ga0.82 V0.18) O1.94
Ga0.82LiO1.94V0.18
Inorganic Materials (USSR) (see: Izv.Akad.Nauk, Neorg.Mater.) (2001) 37, 281-285
a=5.395Å b=6.367Å c=5.0039Å
α=90° β=90° γ=90°
(Ca0.88 Mg1.12) (Si O4)
Ca0.88Mg1.12O4Si
Crystallography Reports (2008) 53, 1107-1111
a=6.3574Å b=4.8164Å c=11.0387Å
α=90° β=90.3° γ=90°